Insulation level: 180C ° C
Soflex® BT25900 is a flexible composite material made of a polyimide film coated on both sides with an adhesive, laminated to a polyester fiber nonwoven and impregnated with an H-grade resin in a low-temperature semi-curing process.
Basic characteristics
• Good heat resistance and good dielectric and mechanical properties
• Can cure at low temperatures and firmly adhere to metal surfaces
• Compatible with most adhesives, resins, and paints
Soflex® BT25900 is a flexible composite material made of a polyimide film coated on both sides with an adhesive, laminated to a polyester fiber nonwoven and impregnated with an H-grade resin in a low-temperature semi-curing process.
Thickness (mm) | Standard width (mm) | Optional width (mm) |
0.20 | 1000 | 2.5~1000 |
0.25 | 1000 | 2.5~1000 |
0.30 | 1000 | 2.5~1000 |
Soflex® BT25900 tubing cores with an inside diameter of 3 inches can be supplied in full rolls or cut into strip trays or sheets in lengths to suit the customer's requirements.
Suitable for class H dry-type transformers as interlayer insulation, class H motors as slot insulation, turn-to-turn insulation and liner insulation.
Storage suggestions
1. Store in a dry and clean room at room temperature.
2. Do not approach sources of fire, heating, or direct sunlight.
3. The storage period is generally 3-6 months. If it exceeds the storage period and passes the technical standard inspection, it can still be used.